White Zirconia disc ST 1200Mpa Translucency 43%
White Zirconia disc ST 1200Mpa Translucency 43%, with a compressive strength of 1200 MPa and a transparency of 43%, is a high-strength ceramic material with excellent mechanical properties and aesthetic appearance. It is mainly composed of zirconium dioxide (ZrO₂), which is sintered at high temperature to form a strong crystal structure that can withstand huge bite forces and long-term wear. The translucent quality imitates the natural appearance of teeth and is suitable for making crowns, bridges, inlays and veneers. It has excellent biocompatibility and is safe and reliable.
- Product Introduction
Products Description
White Zirconia disc ST 1200Mpa Translucency 43%, with a compressive strength of 1200 MPa and a transparency of 43%, is a high-strength ceramic material with excellent mechanical properties and aesthetic appearance. It is mainly composed of zirconium dioxide (ZrO₂), which is sintered at high temperature to form a strong crystal structure that can withstand huge bite forces and long-term wear. The translucent quality imitates the natural appearance of teeth and is suitable for making crowns, bridges, inlays and veneers. It has excellent biocompatibility and is safe and reliable.
| Step | Start Temperature (°C) | End Temperature (°C) | Time (Min) | Speed (°C/min) |
|---|---|---|---|---|
| 1 | Room Temperature | 300 | 40 | 7.5 |
| 2 | 300 | 800 | 100 | 5 |
| 3 | 800 | 1300 | 200 | 2.5 |
| 4 | 1300 | 1530 | 46 | 5 |
| 5 | 1530 | 1530 | 120 | holding |
| 6 | 1530 | Room Temperature | -121.0 | Natural Cool |
Tips: The maximum speed is recommended to be less than 20°C/min. Keep the furnace door closed until the temperature drops to room temperature for natural cooling.
| Step | Start Temperature (°C) | End Temperature (°C) | Time (Min) | Speed (°C/min) |
|---|---|---|---|---|
| 1 | Room Temperature | 300 | 100 | 2.5 |
| 2 | 300 | 960 | 100 | 6.6 |
| 3 | 960 | 1530 | 407 | 1.4 |
| 4 | 1530 | 1530 | 120 | Holding |
| 5 | 1530 | 900 | 60 | 10.3 |
| 6 | 900 | Room Temperature | -121.0 | Natural Cool |
Tips: The maximum speed is recommended to be less than 20°C/min. Keep the furnace door closed until the temperature drops to room temperature for natural cooling.
factory
Cover Area
years experience
Customer Services
Exported Countries
Products certificates
Products certificates
Hot Tags: dental zirconia,zirconia,cad cam,dental,dental lab,zirconia block,zotion